H62 brass sheet

Copper Alloys No.

Materials

Temper

Dimensions (mm)

Main Properties

Thicknesses

Widths

Length

C28000(H62)C27200(H63)

C26800(H68)
C27000(H65)

C26000(H70)

C23000(H85)

Brass Plates with hot rolled

Hot Rolled

4~8

600~2000

4000 max.

When thickness is 4~14mm,

For C27200(Cu62) Rm (min.):290Mpa, A11.3(min.)30%.

For C26200(Cu68),Rm (min.):290Mpa,

A11.3(min.): 40%.

8~60

600~3000

6000 max.

60~120

600~2000

4000 max.

C28000(H62)C27200(H63)

C27000(H65)
C26800(H68)

C26000(H70)

C23000(H85)

C22000(H90)

Brass Sheets and Plates with cold rolled

Soft, Hard

0.5~3.0

1000 max.

2500 max.

3.0~10

3000 max.

6000 max.

Soft, H/2,

 Hard

0.5~3.0

1000 max.

2500 max.

3.0~10

3000 max.

6000 max.

Soft, H/4, H/2, Hard,

Extra Hard.

0.5~3.0

1000 max.

2500 max.

3.0~10

3000 max.

6000 max.

Soft, H/2,

 Hard,

Extra Hard

0.5~3.0

1000 max.

2500 max.

3.0~10

3000 max.

6000 max.

C37000

(HPb59-1)

Free Cutting Muntz metal

Hot Rolled

4.0~8.0

550 max.

3000 max.

When Thickness is 4 to 14mm,
Rm(min.):370Mpa, A11.3(min.):18%.

8.0~60

600 max.

6000 max.

60~80

630 max.

4000 max.

C37000

(HPb59-1)

Soft
H/2
Hard.

3.0~10

550 max.

400 max.

C46400

(HSn62-1)

Naval Brass

Hot Rolled

4.0~8

600~2000

4000 max.

When Thickness is 4 to 14mm,
Rm (Min.): 340Mpa A11.3(min.):20%

8~60

600~3000

6000 max.

Hard
H/2
Soft

0.5~3.0

550 max.

2000 max.